HindiOKT increased fire resistance organosilicon rubber mix
OKT increased fire resistance organosilicon rubber mix is available both with and without added curing agent. The rubber mix is non-toxic, it has FV 0 flammability class. Products made from OKT rubber mix have the following properties: high tracking and erosion resistance, good electrical insulating properties in wet condition, high resistance to ozone, UV rays, precipitation and pollution, weather temperature fluctuations. OKT rubber mix products working temperature conditions are from -50 °С to +200 °С. OKT increased fire resistance rubber mix is intended for manufacture of various rubber products. It can also be used for manufacture of polymer housings of high-voltage insulators and other electrical products.
OKT increased fire resistance rubber mix is intended for manufacture of various rubber products. It can also be used for manufacture of polymer housings of high-voltage insulators and other electrical products.
Specification 2512-078-05766764-2009
Technical characteristics
|
Parameters |
Values |
|
Rollability, minutes, minimum |
5 |
|
Density, g/cm3, maximum |
1.45 |
|
Cured properties: |
|
|
Nominal tensile strength, MPa, minimum |
4.0 |
|
Elongation at break, %, minimum |
300 |
|
Shore A hardness, units, within the range of |
58-70 |
|
Electrical performance after soaking in water at (20±2) °C for 24 hours: |
|
|
Volume resistivity, Ohm·cm, minimum |
1∙1014 |
|
Tan δ, maximum |
0.04 |
|
Dielectric strength at 50 Hz, kV/mm, minimum |
18 |
|
Permittivity, maximum |
5.0 |
|
Flammability rating |
Class FV 0 |
|
Tracking and erosion resistance |
Class 1 A 4.5
(1 V 4,5) |
Packing:
In the form of up to 10 kg pieces. The pieces are wrapped in polyethylene film and placed in a polyethylene bag. Then polyethylene bag with rubber mix is packed in synthetic fabric bags. Net weight of one bag is not more than 30 kg.
Guaranteed shelf life:
Type I: with added curing agent – 3 months, without added curing agent – 6 months
Type II: with added curing agent – 2 months, without added curing agent – 6 months
Guarantee:
The product is manufactured according to the Specification. The product meets the stated information within the shelf life and subject to storage conditions.